PEI ULTEM™ 9085
Sep 16

PEI ULTEM™ 9085

PEI ULTEM™ 9085 (Polyether Imide) is a high performance polymer with excellent mechanical performance. PEI ULTEM™ 9085 is a material from SABIC. This material is UL 94-V0 rated and has a glass transition temperature Tg of 186°C PEI ULTEM™ 9085 is perfect for applications in for example the aerospace automotive and electrical industry. This material is a combination of exceptional dimensional stability, inherent flame retardancy, excellent thermal properties and good chemical resistance.

PEI ULTEM™ 9085 features:

  • Low smoke evolution
  • High thermal properties
  • Excellent chemical resistance
  • Flame retardant
  • High glass transition temperature (Tg)
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,34 g/cc
MFI 340ºC/5kgISO 113330 g/10 min
Tensile strength at yieldISO 52788 MPa
Tensile strength at breakISO 52771 MPa
Elongation strain at breakISO 52750%
Elongation strain at yield ISO 5276,7%
Tensile (E) modulus ISO 5273050 MPa
Impact strength - Charpy notched 23˚CISO 17911 kJ/m²
Flammability behaviourUL94V-0
Flexural modulus ISO 1782750 MPa
Flexural strengthISO 17890 MPa
Vicat softening temp. B120ISO 306173°C
Heat deflection temp. AISO 75152°C
DescriptionTestmethodTypical value
Printing temp.Internal method380±15˚C

Colours:

PEI ULTEM™ 9085 is available in 1 colour.

NA1

Packaging:

PEI ULTEM™ 9085 is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ≥120°C. Adhesion is possible on different surfaces. PEI ULTEM™ 9085 can be used on desktop FDM or FFF technology 3D printers able to reach the high required temperatures. Dry the spool before printing: +4 hours at max. 110°C.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.