PEI ULTEM™ 1010
Sep 16

PEI ULTEM™ 1010

PEI ULTEM™ 1010 is an ultra-performance material with exceptional dimensional stability, inherent flame retardant and good chemical resistance. PEI ULTEM™ 1010 is a material from SABIC. This material is an amorphous, amber to transparent thermoplastics with a glass transition temperature (Tg) of 217°C and performs in continuous use up to 170°C. PEI ULTEM™ 1010 offers superior tensile strength and excellent chemical and thermal resistance for an FDM thermoplastic.

PEI ULTEM™ 1010 features:

  • Low smoke evolution
  • High thermal properties 217°C (Tg)
  • Dimensional stability
  • Flame retardant
  • Outstanding strength and amorphous thermoplastic
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,27 g/cc
MFI 340ºC/5kgISO 113311 g/10 min
Tensile strength at yieldISO 527105 MPa
Tensile strength at breakISO 52754 MPa
Elongation strain at breakISO 52760%
Elongation strain at yield ISO 5276%
Tensile (E) modulus ISO 5273200 MPa
Impact strength - Charpy method 23˚CISO 1805 kJ/m²
Flame retardancy
UL94 (1,5mm)V-0
Flexural modulus ISO 1783200 MPa
Flexural strengthISO 178160 MPa
Vicat softening temp. BISO 306 B50211°C
Heat deflection temp. B (0,45 MPa)ISO 75-2200°C
DescriptionTestmethodTypical value
Printing temp.Internal method370±15˚C

Colours:

PEI ULTEM™ 1010 is available in 1 colour.

NA1

Packaging:

PEI ULTEM™ 1010 is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ≥120°C. Adhesion is possible on different surfaces. PEI ULTEM™ 1010 can be used on desktop FDM or FFF technology 3D printers able to reach the high required temperatures. Dry the spool before printing: +4 hours at max. 110°C.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.