LUVOCOM® 3F PEEK CF 9676 BK
Sep 15

LUVOCOM® 3F PEEK CF 9676 BK

LUVOCOM® 3F PEEK CF 9676 BK has outstanding mechanical properties in combination with its excellent thermal and chemical resistance. LUVOCOM® 3F PEEK CF 9676 BK is a material from LEHVOSS. It is a flame retardant polyetheretherketone reinforced with carbon fibers The carbon fiber improves the stiffness and compressive strength enormously This material is suitable for dynamically stressed parts, aerospace applications and applications which require inherent flame resistance.

LUVOCOM® 3F PEEK CF 9676 BK features:

  • Outstanding temperature and chemical resistance
  • Very high strength and stiffness
  • Suitable for dynamically-stressed parts
  • Flame retardant
  • Low smoke and toxic gas emissions
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,36 g/cc
MFI 380ºC/10kgISO 113316 g/10 min
Tensile strength at yieldISO 527126 MPa
Elongation strain at yieldISO 5273,9%
Tensile (E) modulusISO 5277800 MPa
Impact strength - Charpy notched 23˚CISO 179 1eA7 kJ/m²
Flammability Behaviour
UL94V-0
Heat deflection temp. A (1,8 MPa) ISO 75280°C
Mold shrinkageDIN 167420,2-0,4%
DescriptionTestmethodTypical value
Printing temp.Internal method425±25˚C

Colours:

LUVOCOM® 3F PEEK CF 9676 BK is available in 1 colour.

NA1

Packaging:

LUVOCOM® 3F PEEK CF 9676 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ≥110°C. Adhesion is possible on different surfaces. LUVOCOM® 3F PEEK CF 9676 BK can be used on desktop FDM or FFF technology 3D printers able to reach the required temperatures. Dry the spool before printing: 6-8 hours at max. 120°C or 4 hours at 130°C.
*Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PEEK CF 9676 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles. Note: brass nozzles are not allowed this contains copper which is reactive with PEEK.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.