NOVAMID®ID1070

NOVAMID® ID1070 is a strong and ductile 3D printing grade based on PA6. It is a high-quality polyamide, that has been developed as a special product line in order to cope with high demand levels from our Japanese customers. Novamid® ID1070 has seen various applications in various fields and various regions. From car to packaging, Novamid® is supported by an experienced and wide range of experts.

NOVAMID® ID1070 features:

  • Is a pure polyamide 6, and was originally developed many years ago by our Engineering Plastics experts for demanding specialty applications often subjected to extreme heat
  • The optimized crystallization profile improves fusion, enabling parts with excellent interlayer strength and high surface quality.
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Maximum tensile stress (3D printed tensile bars) 0°-90° ISO 527-1/-245 MPa
Maximum tensile stress (3D printed tensile bars) 45°-45°ISO 527-1/-250 MPa
Tensile modulus (3D printed tensile bars) 0°-90° ISO 527-1/-21710 MPa
Tensile modulus (3D printed tensile bars) 45°-45°ISO 527-1/-22120 MPa
Elongation at break (3D printed tensile bars) 0°-90°ISO 527-1/-27,2%
Elongation at break (3D printed tensile bars) 45°-45°ISO 527-1/-215%
DescriptionTestmethodTypical value
Printing temp.260±10°C
Melting temperature (10°C/min)ISO 11357-1/-3220°C

Colours:

Novamid® ID1070 is available from stock in:

bk1
wh1

Packaging:

Novamid® ID1070@DSM is available in your own packaging with co-branding from DSM.

Additional info:

Common fused filament fabrication (FFF) equipment should work with Novamid® filaments, direct drive as well as Bowden type extruders. Typical settings for any slicing software (e.g. Slic3R, Cura, Simplify3D) are listed below. Note that for different nozzle diameters the settings should be changed accordingly.


Storage:

In order to prevent moisture pick up and contamination, supplied packaging should be kept closed and undamaged. For the same reason, partially used bags should be sealed before re-storage. Allow the material that has been stored elsewhere to adapt to the temperature in the processing room while keeping the bag closed.