LUVOCOM® 3F PP CF 9928 BK
Mar 30

LUVOCOM® 3F PP CF 9928 BK

LUVOCOM® 3F PP CF 9928 BK is polypropylene copolymer reinforced with carbon fiber. LUVOCOM® 3F PP CF 9928 BK is a material from LEHVOSS. It is suitable for continuous discharging of statically-generated electricity. Recommended for strong and stiff parts.

LUVOCOM® 3F PP CF 9928 BK features:

  • Strong and stiff parts
  • Inherent good chemical resistance
  • ESD surface resistance 107
  • Low warpage
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831 g/cc
Tensile strength at yieldISO 52754 MPa
Elongation strain at yieldISO 5271,2%
Tensile (E) modulusISO 5277000 MPa
Flexural strengthISO 17878 MPa
Flexural modulusISO 1786000 MPa
Vicat softening temp. A ISO 30680°C
Mold shrinkageDIN 167420,2-0,6%
Surface resistanceIEC 60093 ≤10^7Ω
Water absorption 23°CISO 62<0,3%
DescriptionTestmethodTypical value
Printing temp.Internal method225±5˚C

Colours:

LUVOCOM® 3F PP CF 9928 BK is available in the colour black.

NA1

Packaging:

LUVOCOM® 3F PP CF 9928 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ± 65-75˚C. Adhesion is possible on different surfaces. Please consider special PP adhesives for 3D-printing. LUVOCOM® 3F PP CF 9928 BK can be used on all common desktop FDM technology or FFF 3D printers. Level of electrical dissipative properties depends on printing conditions. Dry the spool before printing: 4-6 hours at max. 80°C.
*Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PP CF 9928 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles. 

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.