LUVOCOM® 3F PEKK 50082 NT
Sep 16

LUVOCOM® 3F PEKK 50082 NT

LUVOCOM® 3F PEKK 50082 NT (Polyether Ketone Ketone) is a semi-crystalline thermoplastic in the polyaryletherketone family. LUVOCOM® 3F PEKK 50082 NT is a material from LEHVOSS. This material has a very good layer adhesion and dimensional stability. LUVOCOM® 3F PEKK 50082 NT is unique compared to the standard PEKK materials because it prints semi crystalline and it provides improved printability and layer adhesion. This neat PEKK enables semi-crystalline parts with no warping.

LUVOCOM® 3F PEKK 50082 NT features:

  • Outstanding temperature and chemical resistance
  • Excellent mechanical properties
  • Flame retardant
  • Unique tribological properties
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,27 g/cc
MFI 380ºC/2,16kgISO 113325 g/10 min
Tensile strength at yieldISO 52790 MPa
Elongation strain at yieldISO 5275%
Tensile (E) modulusISO 5273000 MPa
Flexural modulus ISO 1782500 MPa
Flexural strength ISO 178150 MPa
Heat deflection temp. A (1,8MPa)ISO 75 (printed)160°C
Flammability behaviourUL94V-0
Mold shrinkageDIN 167420,2-0,4%
DescriptionTestmethodTypical value
Printing temp.Internal method360±20˚C

Colours:

LUVOCOM® 3F PEKK 50082 50082 NT is available in natural colour.

NA1

Packaging:

LUVOCOM® 3F PEKK 50082 NT is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ≥110°C. Adhesion is possible on different surfaces. LUVOCOM® 3F PEKK 50082 NT can be used on desktop FDM or FFF technology 3D printers able to reach the required temperatures. Dry the spool before printing: 6-8 hours at max. 120°C or 4 hours at 130°C.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.