LUVOCOM® 3F PAHT CF 9891 BK is a 15% carbon fiber reinforced material. LUVOCOM® 3F PAHT CF 9891 BK is a material from LEHVOSS. It is designed for industrial applications, easy to print with low warping an increased layer adhesion. LUVOCOM® 3F PAHT CF 9891 BK is a PA6 based material, it has a low influence from moisture and temperature on dimensional stability and electrical properties.

LUVOCOM® 3F PAHT CF 9891 BK features:

  • Carbon Fiber Reinforced Material (15%)
  • Extremely stiff
  • Designed for industrial applications
  • PA6 based material
  • Low warping and increased layer adhesion
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,24 g/cm³
MFI 250ºC/2,16kgISO 11334 g/10 min
Tensile strength at yieldISO 527120 MPa
Elongation strain at yieldISO 5272%
Tensile (E) modulusISO 52710500 MPa
Impact Strength - Charpy method 23°C Unnotched ISO 179 1eA U 35 kJ/m2
Mold shrinkageDIN 167420,3-0,5%
Water absorption 23°C ISO 62<0,3%
DescriptionTestmethodTypical value
Printing temp.Internal method260±5˚C

Colours:

LUVOCOM® 3F PAHT CF 9891 BK is available in the colour black.

NA1

Packaging:

LUVOCOM® 3F PAHT CF 9891 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is 65-75˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT CF 9891 BK can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C. *Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PAHT CF 9891 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.