LUVOCOM® 3F PAHT 9936 BK
Mar 30

LUVOCOM® 3F PAHT 9936 BK

LUVOCOM® 3F PAHT 9936 BK is an unreinforced polyamide-based formulation. LUVOCOM® 3F PAHT 9936 BK is a material from LEHVOSS. LUVOCOM® 3F PAHT 9936 BK has excellent tensile and impact strength and allows continued operation up to 100°C – 120°C while retaining 50% of its mechanical properties and short-term 160°C.

LUVOCOM® 3F PAHT 9936 BK features:

  • Unreinforced PAHT
  • Optimized surface appearance
  • Designed for industrial applications
  • PA6 based material
  • Low warping and increased layer adhesion
Sizeø toleranceRoundness
1,75mmø 0,05mm95%
2,85mmø 0,10mm95%
DescriptionTestmethodTypical value
Specific gravityISO 11831,25 g/cc
MFI 250ºC/2,16kgISO 11336 g/10 min
Tensile strength at yieldISO 52778 MPa
Elongation strain at yieldISO 5274,4%
Tensile (E) modulusISO 5273400 MPa
Flexural modulus
ISO 1786000 MPa
Flexural strength
ISO 17878 MPa
Vicat softening temp. A ISO 30680°C
Heat deflection temp. A (1,8MPa)ISO 7590°C
Mold shrinkageDIN 167420,3-0,5%
Water absorption 23°C ISO 62<0,3%
DescriptionTestmethodTypical value
Printing temp.Internal method265±10˚C

Colours:

LUVOCOM® 3F PAHT 9936 BK is available in the colour black.

NA1

Packaging:

LUVOCOM® 3F PAHT 9936 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional info:

Recommended temperature for heated bed is ± 60-70˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT 9936 BK can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C.

Storage:

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.