LUVOCOM® 3F filament PAHT 9825 NT is a high temperature resistant polyamide (PA) -based, unfilled material. It has the strength of a PA6 without affecting its printability. LUVOCOM® 3F PAHT 9825 NT is a material from LEHVOSS. 3D-printed components made from this material have high strength and toughness. It has a low influence from moisture and temperature on dimensional stability and electrical properties. Can be used in the automotive industry, textile- and office machinery, apparatus- and precision engineering.
LUVOCOM® 3F PAHT 9825 NT features:
- Unreinforced PAHT
- Designed for industrial applications
- PA6 based material
- Low warping and increased layer adhesion
- Strong and tough parts
|Specific gravity||ISO 1183||1,2 g/cc|
|MFI 250ºC/2,16kg||ISO 1133||4 g/10 min|
|Tensile strength at yield||ISO 527||85 MPa|
|Elongation strain at yield||ISO 527||3,6%|
|Tensile (E) modulus||ISO 527||3400 MPa|
|Heat deflection temp. A (1,8MPa)||ISO 75||90°C|
|Mold shrinkage||DIN 16742||0,3-0,5%|
|Water absorption 23°C||ISO 62||<0,3%|
|Printing temp.||Internal method||265±10˚C|
LUVOCOM® 3F PAHT 9825 NT is available in its natural colour.
LUVOCOM® 3F PAHT 9825 NT is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.
Recommended temperature for heated bed is ± 60-70˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT 9825 NT can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C.
Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.